Einsatzstähle, Case hardening steels
|
Stahlsorte
Kurzname |
Werkstoff-
nummer |
alter
Kurzname |
Lieferzustand
|
IMDS-ID |
Zugfestigkeit
Rm in N/mm² |
Streckgrenze
Re in N/mm² |
Bruchdehnung
A in % |
C10 |
1.0301 |
C 10 |
|
11834273 |
490 - 640 |
295 |
16 |
C10GPb |
1.0302 |
C 10Pb |
|
12356 |
490 - 640 |
295 |
16 |
C15 |
1.0401 |
C 15 |
|
11834358 |
590 - 780 |
355 |
14 |
C15GPb |
1.0403 |
C15 Pb |
|
12432 |
590 - 780 |
355 |
14 |
C10E |
1.1121 |
Ck 10(1.1207)* |
|
11834300 |
490 - 640 |
295 |
16 |
C15E |
1.1141 |
Ck 15(1.1140)* |
|
11834364 |
590 - 780 |
355 |
14 |
C16E |
1.1148 |
(1.1208)* |
|
11834376 |
600 |
- |
- |
16NiCr4 |
1.5714 |
(1.5715)* |
|
11830563 |
900 |
- |
- |
14NiCr10 |
1.5732 |
- |
|
- |
880 - 1180 |
685 |
11 |
15NiCr13 |
1.5752 |
14NiCr14 |
|
11830535 |
1030 - 1320 |
785 |
10 |
10NiCr5-4 |
1.5805 |
- |
|
11830258 |
700 |
- |
- |
18NiCr5-4 |
1.5810 |
- |
|
11830597 |
1100 |
- |
- |
14NiCr18 |
1.5860 |
- |
|
13720 |
1180 - 1370 |
885 |
7 |
17CrNi6-6 |
1.5918 |
17CrNi6-6 |
|
11830568 |
1100 |
- |
- |
15CrNi6 |
1.5919 |
- |
|
13722 |
880 - 1180 |
635 |
9 |
18CrNi8 |
1.5920 |
18CrNi8 |
|
13723 |
1180 - 1420 |
785 |
7 |
20NiCrMo2-2 |
1.6523 |
21NiCrMo2(1.6526)* |
|
11830665 |
780 - 1080 |
590 |
10 |
17NiCrMo6-4 |
1.6566 |
17NiCrMo6(1.6569)* |
|
11830572 |
1000 |
- |
- |
20NiCrMoS6-4 |
1.6571 |
- |
|
11830670 |
1100 |
- |
- |
18CrNiMo7-6 |
1.6587 |
17CrNiMo6 |
|
11830592 |
1080 - 1320 |
785 |
8 |
14NiCrMo13-4 |
1.6657 |
- |
|
11830439 |
1030 - 1330 |
- |
10 |
13Cr2 |
1.7012 |
- |
|
- |
540 - 690 |
635 |
17 |
15Cr3 |
1.7015 |
- |
|
13862 |
690 - 880 |
440 |
11 |
17Cr3 |
1.7016 |
(1.7014)* |
|
11830567 |
700 - 900 |
450 |
11 |
20Cr4 |
1.7027 |
(1.7028)* |
|
13869 |
- |
- |
- |
28Cr4 |
1.7030 |
(1.7036)* |
|
11830733 |
700 |
- |
- |
16MnCr5 |
1.7131 |
16MnCr5(1.7139)* |
|
11830552 |
780 - 1080 |
590 |
10 |
20MnCr5 |
1.7147 |
20MnCr5(1.7149)* |
|
11830650 |
980 - 1270 |
685 |
8 |
16MnCrB5 |
1.7160 |
- |
|
11830554 |
900 |
- |
- |
18CrMo4 |
1.7243 |
(1.7244)* |
|
11830585 |
900 |
- |
- |
15CrMo5 |
1.7262 |
- |
|
13933 |
780 - 1080 |
590 |
10 |
20CrMo5 |
1.7264 |
- |
|
13935 |
980 - 1270 |
685 |
8 |
23CrMoB3-3 |
1.7271 |
23CrMoB3-3 |
|
13936 |
1080 - 1370 |
785 |
8 |
20CrMoS2 |
1.7311 |
20 CrMo 2 |
|
13941 |
780 - 1080 |
590 |
10 |
20MoCr3 |
1.7320 |
(1.7319)* |
|
11830658 |
800 |
- |
- |
20MoCr4 |
1.7321 |
20MoCr5(1.7323)* |
|
11830659 |
780 - 1080 |
590 |
10 |
25MoCr4 |
1.7325 |
25MoCr4(1.7326)* |
|
13948 |
980 - 1270 |
685 |
8 |
22CrMoS3-5 |
1.7333 |
22CrMoS-3-5 |
|
11830688 |
- |
- |
- |
* - Diese Stähle gibt es auch mit
einem Schwefelgehalt von 0.020 - 0.040%. Dann wird z.B. C15E = C15R
bzw. Ck15 = Cm15 oder erhalten den Zusatz S (z.B. 20Cr4 = 20CrS4).Werkstoffnummer
in Klammern. Die mechanischen Eigenschaften sind identisch.
+A = Weichgeglüht, +FP = Behandelt auf Ferrit-Perlit Gefüge
und Härtespanne.
Alle Angaben für ø 30 mm und ohne Gewähr |
|
|